Product Description
Product Name
Standard High-Res Resin
Description
An ABS-like SL resin designed for solid-state SLA platforms. Used in master patterns, concept models, general parts, and functional prototypes in the automotive, medical, and consumer electronics industries. Accurate and durable with parts that can stay durable for over 6.5 months.
Typical Features
Liquid Resin’s Viscosity
Medium viscosity for easy recoating and easy cleaning of parts and machines
Improved Strength Retention
Improved strength retention of parts in humid conditions
Minimal Part Finishing
Requires minimal part finishing
Long Shelf Life
Long shelf life in the machine
Typical Benefits
Less Part Finishing Time
Need less part-finishing time, easier post-curing
Accurate and High-Tough Parts
Builds accurate and high-tough parts with
improved dimensional stability
High-Quality Controls
High-quality controls for vacuum casting parts
Low Shrink and Yellowing Resistance
Low shrink and good resistance to yellowing
Magnificent White Color
Produces a magnificent white colour
Machinable SLA Material
Outstanding machinable SLA material
Physical Properties – Liquid Material
Appearance
White
Density
1.13 g/cm3 at 25°C
Viscosity
355cps at 28°C
DP
0.145mm
EC
9.3 mJ/cm3
Building Layer Thickness
0.1mm
Mechanical Properties of Post-Cured Material
Hardness (Shore D)
83 (ASTM D2240)
Flexural Modulus
2692-2775 (ASTM D790)
Flexural Strength
69-74 (ASTM D790)
Tensile Modulus
2189-2395 (ASTM D638)
Elongation at Break
27-31 (ASTM D638)
Impact Strength, Notched Izod, J/m
12-20% (ASTM D638)
Heat Deflection Temperature
58-70°C (ASTM D256)
Glass Transition, Tg
52 (ASTM D648@66PSI)
Coefficient of divermal Expansion
97*E-6 TMA (T<Tg) 1.16
Product Description
Product Name
High Toughness Resin
Description
An ABS-like material with super toughness, high hardness, and high strength. Suitable for producing thin-walled parts with a thickness of 2.5mm and resistant to temperature 70°C. It has excellent detail, small molding shrinkage, good dimensional stability, durability, and can meet the requirements of painting. Suitable for parts with high impact and shock absorption.
Key Benefits
Rigid and Precision Material
Rigid, precision plastic-like injection molding ABS
Temperature Resistance
Resistant to temperature of 65-70°C
Versatile Applications
Suitable for functional prototypes, tools, electrical components, chassis, and phone covers
Post-processing Options
Post-processing includes painting, bonding, or metalization
3D Printing System Compatibility
Suitable for SLA light-curing 3D printing system with a light source of 355nml
Mechanical Properties of Post-Cured Material
Heat Deflection Temperature(0.46 MPa)
56°C
Hardness (Shore D)
86
Tensile Strength
51.21 MPa
Tensile Modulus
2136 MPa
Flexural Strength
93.5 MPa
Flexural Modulus
2155 MPa
Impact Strength
27 J/m
Product Description
Product Name
High Temp Resin

Description
A stereolithography resin with high temperature resistance and high
precision. The printed workpiece is a specialgray colorand is
used in the stereolithography method of SLA. Widely used in the production
of models and parts for industrial prototypes, automobiles, medical care,
shoe molds, household appliances, mobile phones,home automation, building materials, and consumer electronic products.

Typical Features
High Precision
Compared with ordinary products on the market, the
shrinkage ratio will be reduced by 30%.

Physical Properties – Liquid Material
Appearance
White

Proportion
1.1 g/cm3 at 25°C

Viscosity
580cps at 28°C

DP
0.10mm

EC
9.8 mJ /cm3

Building Layer Thickness
0.1mm

Mechanical Propertiesof Post-Cured Material
Hardness (Shore D)
85D (ASTM D2240)

Flexural Modulus
2900-3220 (ASTM D790)

Flexural Strength
64-69 (ASTM D790)

Tensile Modulus
1900-2090 (ASTM D638)

Tensile Strength
40-44 (ASTM D638)

Elongation at Break
13-20% (ASTM D638)

Impact Strength, Notched Izod, J/m
34.4 (ASTM D256)

Heat Deflection Temperature
99.6°C (ASTM D648@66PSI)

Product Description
Product Name
Clear Resin
Description
A clear SL resin with accurate and durable features. Designed for solid state SLA platforms, Crysta-8QEF1 can be applied in master patterns, concept models, general parts, and functional prototypes in dive automotive, medical, and consumer electronics industries.
Typical Features
Medium Viscosity
Liquid resin‘s medium viscosity makes it easy to recoat and clean parts and machines
Improved Strength and Dimension Retention
Improved strength retention and dimensions retention of parts in humid conditions
Minimal Part Finishing
Requires minimal part finishing
Easy to Burn Completely
Easy to burn completely
Typical Benefits
Superior Clarity
Builds parts with outstanding clarity and excellent accuracy
Less Part Finishing Time
Need less part finishing time, easier post-curing
Suitable for Casting
Suitable for casting
Physical Properties – Liquid Material
Appearance
Clear
Density
1.12 g/cm3 at 25°C
Viscosity
312-420 cps at 28°C
DP
0.18mm
EC
9.8-12 mJ/cm3
Building Layer Thickness
0.1mm

General and Mechanical Properties

Property Measurement Test Method Value
Powder Melting Point ASTM D3418 186°C / 367°F
Particle Size ASTM D3451 58μm
Powder Density ASTM D1895 0.48 g/cm3 (0.017 lb / inch3)
Component Density ASTM D792 1.3 g / cm3 (0.047 lb / inch3)
Tensile Strength, maximum load (XY) ASTM D638 30 MPa/4350 psi
Tensile Strength, maximum load (Z) 11 ASTM D638 30 MPa/4350 psi
Tensile Strength ASTM D638 2900 MPa/421 ksi
Tensile Modulus ASTM D638 2900 MPa/406 ksi
Elongation at Break ASTM D638 6.5%
Impact Strength, Notched Izod ASTM D256 2.7 KJ/m2
Heat Deflection (0.45 MPa, 66 psi) (Z) ASTM D648 173°F/344°F A
Heat Deflection (1.82 MPa, 264 psi) (Z) ASTM D648 121°F/250°F

Click to view spec from HP

 

EnvisionTEC RC Series are high-temperature resins for building tough and stiff parts at very high resolutions. Parts made with these materials are ideal for silicone molding, pump housings, blades, test parts for wind tunnels, light reflectors and various automotive applications.

These materials are also perfect for high detail jewelry and animation applications and can be finished with a variety of methods including painting or plating.

EnvisionTEC RC25/RC30 High-Temperature Resins Properties

Material Properties Value
Tensile Strength 46 MPa
Elongation at Break 2.5%
Flexural Strength 102 MPa
Flexural Modulus 3860 MPa
Izod Impact – Notched 0.0016 KJ/m2
Hardness 93.1 Shore D
Heat Deflection Temperature at 0.46 MPa 67°C
Heat Deflection Temperature at 1.81 MPa 53.6°C

Click to view spec from EnvisionTEC